RECOMMENDED FOR
Waterproofing and protection of:
- Tiles
- natural stone
- wood
- verandas and balconies
- terraces
- Also suitable for sealing concrete (Applied in thick, bubble-free, coats)
LIMITATIONS:
- Not recommended for unsound substrates,
- Non-porous substrates, such as ceramic tiles must be primed with PRIMER-T first.
APPLICATION PREREQUISITES
Can be successfully applied on:
Tiles, concrete, cement roof tiles, wood, corroded metal, galvanized steel. For information about other substrates, please contact our tech department.
Concrete substrate conditions (standard):
- Hardness: R28 = 15 Mpa
- Humidity: W < 10%
- Temperature: 5-35 oC
- Relative humidity: < 85%
Primer selection for special conditions and substrates: Please refer to the Primer Selection Table.
APPLICATION PROCEDURE
Clean the surface using a high pressure washer, if possible. Remove oil, grease and wax contaminants. If used for concrete sealing, cement laitance, loose particles, mould release agents, cured membranes must also be removed. Fill surface irregularities with the necessary product.
Priming:
Priming is required when application is on non-porous substrates, such as ceramic tiles and marble. In this case, PRIMER-T is used. It is applied with a clean cloth without leaving any pools of fluid (apply as if wiping the surface).
Mixing:
Stir well, manually or with a low speed mixer. No thinning is required but SOLVENT-01 may be used.
Application:
HYPERDESMO-T is applied as soon as the primer dries (after 15-20 minutes) with roller in one or two coats. Do not leave more than 24 hours between coats.
CONSUMPTION
Minimum total consumption: 0.2-1.0 kg/m2.
CLEANING
Clean tools and equipment first with paper towels and then using SOLVENT-01. Rollers will not be re-usable.
PACKAGING
1 kg, 5 kg, 20 kg and 200 kg drums.
SHELF LIFE
Can be kept for 12 months minimum in the original unopened pails in dry places and at temperatures of 5-25 oC. Once opened, use as soon as possible.
TECHNICAL SPECIFICATIONS
In liquid form (before application): 80% dry matter in Xylol.
PROPERTY |
UNITS |
METHOD |
SPECIFICATION |
Viscosity (Brookfield) |
cP |
ASTM D2196-86, @ 25 oC |
1,000 |
Specific weight |
gr/cm3 |
ASTM D1475 / DIN 53217 / ISO 2811,
@ 20 oC |
1.0 |
Solids |
% |
internal |
80-85 |
Flash point |
oC |
ASTM D93, closed cup |
42 |
Tack free time, @ 77 oF (25
oC) & 55% RH |
hours |
– |
6 |
Recoat time |
hours |
– |
6-24 |
In cured form (after application):
PROPERTY |
UNITS |
METHOD |
SPECIFICATION |
Service temperature |
oC |
– |
-40 to 80 |
Max. temperature short time (shock) |
oC |
– |
200 |
Hardness |
Shore D |
ASTM D2240 / DIN 53505 / ISO R868 |
40 |
Tensile strength at break @ 23 oC |
Kg/cm2 (N/mm2) |
ASTM D412 / EN-ISO-527-3 |
350
(35) |
Percent elongation @ 23 oC |
% |
ASTM D412 / EN-ISO-527-3 |
> 350 |
Water vapor transmission |
gr/m2.hr |
ASTM E96 (Water Method) |
0.8 |
QUV Accelerated Weathering Test (4hr UV, @ 60 oC (UVB- Lamps) & 4hr COND @ 50
oC) |
– |
ASTM G53 |
passed (3,000 hours) |
Thermal resistance (100 days @ 80 °C) |
– |
EOTA TR011 |
passed |
Chemical (hydrolysis) resistance:
Potassium Hydroxide, 8% |
10 days @ 50 oC |
unaffected |
Sodium Hypochlorite, 5% |
10 days |
unaffected |
Water absorption |
– |
< 1.4% |